Description
- Glass Flame Retardant protective sheeting ranges from 0.3mm to 1mm in thickness.
- Offering the greatest transparency on the market, it is made exclusively of non-phthalate plasticisers.
- This is an extremely important factor since it means the product does minimal harm to humans or the environment, compared with other products of a similar nature.
- Flame retardant, our CoruGlass Flame Retardant film provides the preferred solution for numerous applications, thanks to its high transparency, UV resistance and durability.
- As well as being used for protective sheets in the fight against viruses, it is ideal for other applications such as tents, marquees, porch roofs, boats (including awning), terraces, canopies, doors, windows, cars, yachts and any partition.
| Colour | No |
|---|---|
| Resistance to | No |
| Insertion Req | No |
| Material | No |
| Shore Hardness +/- 5º | No |
|
Property |
Test method/method |
Technical data |
|
Colour |
|
Clear |
|
Density |
DIN 53479/A |
1.25g/cc+/-0.05 |
|
Tear strength |
ISO 6383-1:1983 |
Crosswind: 46.5N/mm |
|
Lengthways: 38.5N/mm |
||
|
Tensile strength Test |
ISO527-1:2012 &ISO 527-3:1995/Cor. 2:2001 |
crosswide: 20.1mpa |
|
Lengthways: 21.2mpa |
||
|
Elongation at break: |
ISO527-1:2012 &ISO 527-3:1995/Cor. 2:2001 |
crosswide: 292% |
|
Lengthways: 275% |
||
|
Flammability |
DIN 53382/DIN4102/B2 |
Normally flammable B2 |
|
Edge fire behaviour |
DIN53382/2/DIN4102/B2 |
Self-extinguishing |
|
Fire Behaviour |
DIN53382/2/DIN4102/B2 |
Doesn’t continue to burn or smoulder |
TEST RESULTS:
- These tests are conducted in DIN4102-1 Clause 6.2 Class B2 materials according to the application.
1 Samples details:
|
Materials/colour |
|
PVC/Transparent |
|
|
Thickness |
|
2mm |
|
|
2 Test Conditions |
|
|
|
|
|
Temperature |
Relative Humidity |
Duration |
|
Precondition |
T=23+/-2 ℃ |
(50+/-6)% |
8 days |
3 Test requirements:
- Class B2: This test shall be deemed passed if for any of the five specimens tested flaming does not reach the gauge mark within 20 seconds after flame application, either with bottom edge ignition or surface ignition.
4 Test Result:
- The test result was obtained using the specified test condition and does not necessarily represent the behaviour of the test material under other conditions of test or use.
|
Parameter |
Result |
||||||||||||||||||
|
Bottom Edge Ignition |
Surface Ignition |
||||||||||||||||||
|
1 |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
||||||||||
|
Specimen Ignition Y/N |
Y |
Y |
Y |
Y |
Y |
Y |
Y |
Y |
Y |
Y |
|||||||||
|
Ignition Ceased Time |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
|||||||||
|
If flame tip reached 150mm Line/40, 190mm line |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
|||||||||
DIN4102-1B2 TEST RESULT
|
Ignition time to reach 150mm line/40,190mm line |
- |
- |
- |
- |
- |
- |
- |
- |
- |
|
|
Filter paper ignition |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
NO |
NO |